Find the most up-to-date version of ASTM D at Engineering Supersedes: ASTM D Alert Withdrawn. Number of Included in: ASTM Volume ICS: – Volume – Textiles (II): D – LATEST. D – Designation: D – 04 Standard Test Method for Strap 1 This test method is under the jurisdiction of ASTM Committee D13 on.
|Published (Last):||21 April 2012|
|PDF File Size:||8.63 Mb|
|ePub File Size:||1.29 Mb|
|Price:||Free* [*Free Regsitration Required]|
Your Alert Profile lists the documents that will be monitored. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.
Precision and Bias Please first log in with a verified email before subscribing r4393 alerts. Adhesion test compounds are usually replaced after six months; however, some may require replacement within a few weeks.
Since there is a characteristic peak in force at beginning of peel, ignore the? Exercise caution in sampling and handling so that samples receive minimum exposure to ambient atmosphere prior to rubber embedment.
It is the responsibility of the user of this asttm to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. A superscript epsilon e indicates an editorial change since the last revision or reapproval.
Proceed to peel this second r4393 fabric interface. Remove holland cloth backing and lay freshly-exposed surface up on a clean, nonstick surface.
The force to peel one fabric layer from the other is determined in a recording tensile testing machine. NOTE 1—A realistic speci?
Material Test Machines and Equipment
It is the responsibility of the user asm this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. This test method may be used to evaluate cords and fabrics in industrial hose and belting products and other cord or fabric reinforced rubber products.
It is applicable to either woven or parallel cord textile structures from both natural and manmade fibers and to parallel steel cord str. It is applicable to either woven or parallel cord textile structures from both natural and manmade fibers and to parallel steel cord structures. As the voice of the U. Remove the specimen from the hot mold as quickly as possible and air-cool the specimen.
Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. This test method may be used to evaluate cords and fabrics in industrial hose and belting products and other cord or fabric reinforced rubber products. Link to Active Ast link will always route to the current Active version of the standard.
You can download and open this file to your own computer but DRM prevents opening this file on another computer, including a networked server. Either system of units may be used in this test method. This ensures that you are always up-to-date and saves you both time and money. These two fabrics are laid one against the other, with cords in the same direction, to form the pad Fig.
Remove the specimen s from the hot platens as quickly as possible after curing is completed, and cool the specimen at ambient temperature. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters.
Remove atsm cloth backing and place freshly-exposed surface against top of the? This test method 4d393 a good comparison of variables on adhesion because it produces both an qstm numerical value of peel force over several linear centimetres of cord and provides convenient specimens for r4393 appearance see For steel cord, Test Method D provides convenient and rapid adhesion results.
Determine adhesion force by one of the options in D — 04 appropriate for the cure aatm of the rubber stock. Please first verify your email before subscribing to alerts. Holland cloth or other nonstick material should be used as the outside layer on either side of the? The moment new editions of the standards you monitor are released, changes are made, or appendixes are published, you will be alerted by email.
Read more about subscriptions. This test method may be used to evaluate cords and fabrics in industrial hose and belting products and other cord or fabric reinforced rubber products. It may be used for purchase speci? In place of the additional rubber or as a part thereof on the outer sides of the primary fabric-rubber-fabric sandwich, place on the following: Stay on Page Continue to Compass.
This standard is also available to be included in Standards Subscriptions. Add to Alert PDF. For steel cord, it may be required to use a backing fabric in place of the additional rubber or portion thereof in order to maintain integrity of the specimen during peeling on the tensile test machine.
If a bias is found, either its cause must be found and corrected or the purchaser and the supplier must agree to interpret future test results in the light of the known bias.
Current edition approved Oct. The inch-pound units in parentheses are provided in this test method are not necessarily exact equivalents of the SI units. This test method may be used to evaluate tire cord adhesives fabric dipmetallic usually brass coatings on steel cord, and the process of adhesive reaction on the cord using one consistent form of tire cord or fabric and one consistent rubber compound. Rubber moisture content less than 0.
Nevertheless, the expected range of values which characterize acceptable adhesion can be determined in any cord-rubber combination with experience.
Formerly under the jurisdiction of F4393 D13 on Textiles, this test method was withdrawn in February Start Webshop Product catalog Product presentation.
Summary of Test Method 4. This test method covers the determination of peel adhesion of reinforcing fabrics that are bonded to rubber compounds. Apparatus and Materials 6.